Section |
Dimensions |
Mass |
Moment of inertia |
Modulus of Section |
|||
Width |
Height |
Thickness |
Per pile |
Wall |
|
|
|
w |
h |
t |
|
|
|
|
|
mm |
mm |
mm |
kg/m |
kg/m2 |
cm3/m |
cm4/m |
|
OZ 13A |
675 |
399 |
6.5 |
55.5 |
82.2 |
1,370 |
27,251 |
OZ 14A |
675 |
399 |
7 |
59.7 |
88.5 |
1,470 |
29,281 |
OZ 15A |
675 |
400 |
7.5 |
64 |
94.8 |
1,570 |
31,325 |
OZ 16A |
675 |
400 |
8 |
68.2 |
101.1 |
1,670 |
33,350 |
OZ 17A |
685 |
401 |
8.5 |
72.3 |
105.6 |
1,780 |
35,558 |
OZ 18A |
685 |
401 |
9 |
76.6 |
111.8 |
1,880 |
37,580 |
OZ 19A |
685 |
402 |
9.5 |
80.8 |
118.0 |
1,970 |
39,595 |
OZ 20 |
650 |
437 |
8 |
70.8 |
108.9 |
1,980 |
43,290 |
OZ 20A |
685 |
402 |
10 |
85.1 |
124.2 |
2,070 |
41,601 |
OZ 21 |
650 |
438 |
8.5 |
75.1 |
115.5 |
2,100 |
45,910 |
OZ 22 |
650 |
438 |
9 |
79.4 |
122.2 |
2,220 |
48,520 |
OZ 23A |
650 |
439 |
9.5 |
83.6 |
128.6 |
2,330 |
51,120 |
OZ 24A |
650 |
439 |
10 |
87.9 |
135.2 |
2,450 |
53,710 |
OZ 25A |
650 |
440 |
10.5 |
92.3 |
142 |
2,560 |
56,387 |
OZ 26 |
675 |
440 |
10.5 |
95.9 |
142.1 |
2,620 |
57,410 |
OZ 27 |
675 |
440 |
11 |
99.8 |
147.9 |
2,730 |
60,043 |
OZ 28A |
675 |
441 |
11.5 |
104.4 |
154.6 |
2,850 |
62,667 |
OZ 29A |
675 |
441 |
12 |
108.9 |
161.3 |
2,960 |
65,281 |
OZ 31A |
675 |
442 |
12.7 |
115.2 |
170.7 |
3,120 |
68,927 |
OZ 32 |
675 |
487 |
11 |
108.3 |
160.4 |
3,180 |
77,370 |
OZ 33 |
675 |
488 |
11.5 |
113.1 |
167.6 |
3,320 |
80,750 |
OZ 34A |
675 |
488 |
12 |
117.8 |
174.5 |
3,450 |
84,120 |
OZ 36 |
675 |
489 |
12.5 |
122.5 |
181.5 |
3,580 |
87,470 |
OZ 37 |
675 |
489 |
13 |
127.3 |
188.6 |
3,720 |
90,830 |
OZ 38A |
675 |
490 |
13.5 |
132 |
195.6 |
3,850 |
94,170 |
OZ 40 |
675 |
490 |
14 |
136.6 |
202.4 |
3,980 |
97,490 |
OZ 40-700 |
700 |
600 |
11 |
117.2 |
167.4 |
4,000 |
120,087 |
OZ 41A-700 |
700 |
600 |
11.5 |
122.5 |
175 |
4,170 |
125,137 |
OZ 43-700 |
700 |
600 |
12 |
127.8 |
182.6 |
4,340 |
130,151 |
OZ 45-700 |
700 |
600 |
12.5 |
133.2 |
190.2 |
4,500 |
135,130 |
OZ 46A-700 |
700 |
600 |
13 |
138.5 |
197.8 |
4,670 |
140,075 |
OZ 48-700 |
700 |
600 |
13.5 |
143.8 |
205.4 |
4,830 |
144,986 |
OZ 50-700 |
700 |
600 |
14 |
149.1 |
213 |
5,000 |
149,862 |
OZ 50A-700 |
700 |
600 |
14.2 |
151.3 |
216.1 |
5,070 |
151,970 |
OZ 51-700 |
700 |
600 |
14.3 |
152.3 |
217.6 |
5,100 |
153,024 |
OZ 51A-700 |
700 |
600 |
14.5 |
154.5 |
220.7 |
5,170 |
155,135 |
OZ 27W-750 |
750 |
560 |
10 |
96.9 |
129.3 |
2,719 |
76,138 |
OZ 28W-750 |
750 |
560 |
10.5 |
101.6 |
135.4 |
2,845 |
79,672 |
OZ 29AW-750 |
750 |
560 |
11 |
106.4 |
141.9 |
2,956 |
82,782 |
OZ 31W-750 |
750 |
560 |
11.5 |
111.3 |
148.3 |
3,087 |
86,428 |
OZ 32W-750 |
750 |
560 |
12 |
116.1 |
154.8 |
3,205 |
89,734 |
OZ 33W-750 |
750 |
560 |
12.5 |
120.9 |
161.2 |
3,335 |
93,383 |
OZ 33AW-750 |
750 |
560 |
12.7 |
122.9 |
163.8 |
3,384 |
94,739 |
OZ 34AW-750 |
750 |
560 |
13 |
125.8 |
167.7 |
3,455 |
96,733 |
OZ 35AW-750 |
750 |
560 |
13.5 |
130.6 |
174.1 |
3,575 |
100,095 |
OZ 37W-750 |
750 |
560 |
14 |
135.4 |
180.6 |
3,693 |
103,407 |
OZ Tablestaca Cada uno de estos procesos se produce más en algunas etapas del recorrido de un río y menos durante otras partes del mismo. Cuando se elimina la humedad de la arena verde, se la conoce como arena seca. La fractura de un sólido suele producirse debido al desarrollo de ciertas superficies de discontinuidad por desplazamiento dentro del sólido.
Perfiles en Z Tablestacas laminadas en frío floats El vidrio OZ 50-700 está hecho de silicato de sodio OZ 43-700 y silicato de calcio OZ 45-700 por lo que también se le llama vidrio de cal OZ 46A-700 sódico. La adhesividad es la propiedad de la arena OZ50A-700 debido a la cual las partículas de arena se adhieren a los lados de la caja de moldeo. Los ríos nacen en puntos altos en colinas o montañas y luego se unen a otros arroyos y ríos OZ45-700 en las confluencias.
La colapsabilidad es la propiedad de la arena OZ48-700 debido a la cual el molde de arena OZ 50-700 colapsa automáticamente después de la solidificación de la pieza fundida. Los bloques de vidrio OZ 45-700 o los ladrillos de vidrio OZ 50A-700 se fabrican a partir de dos mitades diferentes OZ 50A-700 y se prensan y se recocen juntas OZ 46A-700 durante el proceso de fusión del vidrio. Aunque OZ46A-700 puede parecer muy lento y tranquilo en su superficie, aún tiene gran poder y continúa transportando sedimentos.