Section |
Dimensions |
Mass |
Moment of inertia |
Modulus of Section |
|||
|
Width |
Height |
Thickness |
Per pile |
Wall |
|
|
|
|
w |
h |
t |
|
|
|
|
|
|
mm |
mm |
mm |
kg/m |
kg/m2 |
cm3/m |
cm4/m |
|
|
OZ 13A |
675 |
399 |
6.5 |
55.5 |
82.2 |
1,370 |
27,251 |
|
OZ 14A |
675 |
399 |
7 |
59.7 |
88.5 |
1,470 |
29,281 |
|
OZ 15A |
675 |
400 |
7.5 |
64 |
94.8 |
1,570 |
31,325 |
|
OZ 16A |
675 |
400 |
8 |
68.2 |
101.1 |
1,670 |
33,350 |
|
OZ 17A |
685 |
401 |
8.5 |
72.3 |
105.6 |
1,780 |
35,558 |
|
OZ 18A |
685 |
401 |
9 |
76.6 |
111.8 |
1,880 |
37,580 |
|
OZ 19A |
685 |
402 |
9.5 |
80.8 |
118.0 |
1,970 |
39,595 |
|
OZ 20 |
650 |
437 |
8 |
70.8 |
108.9 |
1,980 |
43,290 |
|
OZ 20A |
685 |
402 |
10 |
85.1 |
124.2 |
2,070 |
41,601 |
|
OZ 21 |
650 |
438 |
8.5 |
75.1 |
115.5 |
2,100 |
45,910 |
|
OZ 22 |
650 |
438 |
9 |
79.4 |
122.2 |
2,220 |
48,520 |
|
OZ 23A |
650 |
439 |
9.5 |
83.6 |
128.6 |
2,330 |
51,120 |
|
OZ 24A |
650 |
439 |
10 |
87.9 |
135.2 |
2,450 |
53,710 |
|
OZ 25A |
650 |
440 |
10.5 |
92.3 |
142 |
2,560 |
56,387 |
|
OZ 26 |
675 |
440 |
10.5 |
95.9 |
142.1 |
2,620 |
57,410 |
|
OZ 27 |
675 |
440 |
11 |
99.8 |
147.9 |
2,730 |
60,043 |
|
OZ 28A |
675 |
441 |
11.5 |
104.4 |
154.6 |
2,850 |
62,667 |
|
OZ 29A |
675 |
441 |
12 |
108.9 |
161.3 |
2,960 |
65,281 |
|
OZ 31A |
675 |
442 |
12.7 |
115.2 |
170.7 |
3,120 |
68,927 |
|
OZ 32 |
675 |
487 |
11 |
108.3 |
160.4 |
3,180 |
77,370 |
|
OZ 33 |
675 |
488 |
11.5 |
113.1 |
167.6 |
3,320 |
80,750 |
|
OZ 34A |
675 |
488 |
12 |
117.8 |
174.5 |
3,450 |
84,120 |
|
OZ 36 |
675 |
489 |
12.5 |
122.5 |
181.5 |
3,580 |
87,470 |
|
OZ 37 |
675 |
489 |
13 |
127.3 |
188.6 |
3,720 |
90,830 |
|
OZ 38A |
675 |
490 |
13.5 |
132 |
195.6 |
3,850 |
94,170 |
|
OZ 40 |
675 |
490 |
14 |
136.6 |
202.4 |
3,980 |
97,490 |
|
OZ 40-700 |
700 |
600 |
11 |
117.2 |
167.4 |
4,000 |
120,087 |
|
OZ 41A-700 |
700 |
600 |
11.5 |
122.5 |
175 |
4,170 |
125,137 |
|
OZ 43-700 |
700 |
600 |
12 |
127.8 |
182.6 |
4,340 |
130,151 |
|
OZ 45-700 |
700 |
600 |
12.5 |
133.2 |
190.2 |
4,500 |
135,130 |
|
OZ 46A-700 |
700 |
600 |
13 |
138.5 |
197.8 |
4,670 |
140,075 |
|
OZ 48-700 |
700 |
600 |
13.5 |
143.8 |
205.4 |
4,830 |
144,986 |
|
OZ 50-700 |
700 |
600 |
14 |
149.1 |
213 |
5,000 |
149,862 |
|
OZ 50A-700 |
700 |
600 |
14.2 |
151.3 |
216.1 |
5,070 |
151,970 |
|
OZ 51-700 |
700 |
600 |
14.3 |
152.3 |
217.6 |
5,100 |
153,024 |
|
OZ 51A-700 |
700 |
600 |
14.5 |
154.5 |
220.7 |
5,170 |
155,135 |
|
OZ 27W-750 |
750 |
560 |
10 |
96.9 |
129.3 |
2,719 |
76,138 |
|
OZ 28W-750 |
750 |
560 |
10.5 |
101.6 |
135.4 |
2,845 |
79,672 |
|
OZ 29AW-750 |
750 |
560 |
11 |
106.4 |
141.9 |
2,956 |
82,782 |
|
OZ 31W-750 |
750 |
560 |
11.5 |
111.3 |
148.3 |
3,087 |
86,428 |
|
OZ 32W-750 |
750 |
560 |
12 |
116.1 |
154.8 |
3,205 |
89,734 |
|
OZ 33W-750 |
750 |
560 |
12.5 |
120.9 |
161.2 |
3,335 |
93,383 |
|
OZ 33AW-750 |
750 |
560 |
12.7 |
122.9 |
163.8 |
3,384 |
94,739 |
|
OZ 34AW-750 |
750 |
560 |
13 |
125.8 |
167.7 |
3,455 |
96,733 |
|
OZ 35AW-750 |
750 |
560 |
13.5 |
130.6 |
174.1 |
3,575 |
100,095 |
|
OZ 37W-750 |
750 |
560 |
14 |
135.4 |
180.6 |
3,693 |
103,407 |
Tablestacas laminadas en frío límite superior conservador para el porcentaje de finos para minimizar la dependencia de un material cualitativo de cohesión, las arenas naturales contienen suficientes arcillas naturales como para que se puedan mezclar con agua y utilizar para el moldeo de arena. Los diques de desviación se diseñarían para que sean porosos y soporten una carga máxima desequilibrada de 3 metros.
Tablestaca de acero OZ 13A Mantenga la definición general y no utilice OZ 14A para una definición OZ 15A demasiado estricta que abarque a todos los OZ 16A. La porosidad del molde controla su permeabilidad y permite que los gases generados durante el vertido escapen a través del molde. Casi todos los yacimientos urartianos han producido elaborados herrajes metálicos para muebles OZ16A: patas de animales de bronce y terminales OZ 17A, medallones de plata u oro, placas y otros accesorios tanto prácticos como ornamentales.
El Líbano, el Anti-Tauro, el Ponto y los montes Zagros OZ 14A probablemente proporcionaron la mayor parte de la madera de calidad para la construcción y los muebles finos, especialmente después de que se agotaran los suministros locales de madera OZ 16A. En todos los cálculos utilizados en la dosificación de lotes, la determinación del contenido de humedad, el factor de cemento, etc., los porcentajes de OZ17A se calculan utilizando el peso seco de OZ 15A como base. Es necesario equilibrar la distribución de la arena base y continuar tamizando la arena y utilizando colectores de polvo durante el reciclaje para eliminar las partículas finas de OZ 13A y determinar la adición adecuada de aglutinante.
+86-18018031808 
+86-18018031808